Etronit IIQ - Sheets
|
|
 |
|
|
|
|
|
|
| Components: |
Paper - Phenolic |
Back |
| Colour: |
Dark brown |
|
| Serial No: |
030 |
|
| IEC 60893: |
PF CP 203 |
Print version |
| DIN 7735: |
Hp 2061 |
|
| NEMA LI 1: |
XX |
|
|
Previous
| Next
|
| |
 |
|
|
|
|
Testmethod |
Thickness |
Value |
Unit |
|
| Flexural strength at RT |
 |
ISO 178 |
≥1,6 mm |
170 |
MPa |
* 1 |
| Flexural strength at elevated temp. |
|
ISO 178 |
≥1,6 mm |
- |
MPa |
- |
| Modulus of elasticity |
|
ISO 178 |
≥1,6 mm |
8.000 |
MPa |
* 1 |
| Compressive strength |
 |
ISO 604 |
≥5,0 mm |
320 |
MPa |
* 1 |
| Izod impact strength, parallel |
 |
ISO 180/2A |
≥5,0 mm |
3,5 |
KJ/m2 |
* 1 |
| Shearing strength, parallel |
 |
IEC 60893-2 |
≥5,0 mm |
35 |
MPa |
* 1 |
| Tensile strength |
|
ISO 527 |
≥1,6 mm |
140 |
MPa |
* 1 |
|
| Electrical properties |
|
Testmethod |
Thickness |
Value |
Unit |
|
| Electric strength in oil at 90°C |
 |
IEC 243-1 |
3,0 mm |
5 |
kV/mm |
* 2 |
| Electric strength in oil at 90°C |
 |
IEC 243-1 |
≥3,0 mm |
20 |
kV/25mm |
* 2 |
| Permittivity 50 Hz |
|
IEC 250 |
≤3,0 mm |
5,0 |
|
* 3 |
| Permittivity 1 MHz |
|
IEC 250 |
≤3,0 mm |
- |
|
- |
| Dissipation factor 50 Hz |
|
IEC 250 |
≤3,0 mm |
0,05 |
|
* 3 |
| Dissipation factor 1 MHz |
|
IEC 250 |
≤3,0 mm |
- |
|
- |
| Insulation resistance after immersion in water |
|
IEC 167 |
All |
100 |
MΩ |
* 4 |
| Comparative tracking index |
|
IEC 112 |
≥3,0 mm |
100 |
CTI |
* 1 |
|
| Physical and thermal properties |
|
|
Testmethod |
Thickness |
Value |
Unit |
|
| Thermal endurance index 20.000 h |
|
IEC 216 |
≥3,0 mm |
120 |
T.I. |
- |
| Flammability |
|
IEC 707 |
3,0 mm |
- |
|
- |
| Density |
|
IEC 1183-A |
All |
1,35 |
g/cm3 |
* 1 |
| Water absorption |
|
IEC 62-1 |
50x50x3 mm |
200 |
mg |
* 4 |
|
| Characteristics and applications |
|
| Mechanically the best Etronit type with electrical properties adequate for insulation in low-voltage constructions. Construction material in electrical appliances, bus-bar carriers, partition plates, protection materials, etc. |
|
|
|
Notes:
A) Thickness > 8mm.
B) Thickness ≥ 4,0mm
C) 1 h/130°C / measured at 130°C
D) 1 h/150°C / measured at 150°C
E) 1 h/180°C / measured at 180°C
F) 1 h/200°C / measured at 200°C
|
* Conditioning:
1: 24h/23°C/50%RH
2: 24h/23°C/50%RH + 1h/Oil 90°C
3: 96h/105°C + 1h/23°C/20%RH
4: 24h/50°C + 24h/water 23°C
5: 96h/105°C + 1h/Oil 90° |
|
|
|
| The above values are average values based on the results of extensive testing in our laboratories. ELEKTRO-ISOLA A/S cannot accept responsibility for the performance of our products in applications over which we have no control. |
|
|