G-Etronax PI - Sheets
|
|
 |
|
|
|
|
|
|
| Components: |
Glass fabric - Polyimide |
Back |
| Colour: |
Dark brown |
|
| Serial No: |
770 |
|
| IEC 60893: |
PI GC 301 |
Print version |
| DIN 7735: |
- |
|
| NEMA LI 1: |
- |
|
|
Previous
| Next
|
| |
 |
|
|
|
|
Testmethod |
Thickness |
Value |
Unit |
|
| Flexural strength at RT |
 |
ISO 178 |
≥1,6 mm |
450 |
MPa |
* 1 |
| Flexural strength at elevated temp. |
|
ISO 178 |
≥1,6 mm |
360 F) |
MPa |
- |
| Modulus of elasticity |
|
ISO 178 |
≥1,6 mm |
25.000 |
MPa |
* 1 |
| Compressive strength |
 |
ISO 604 |
≥5,0 mm |
650 |
MPa |
* 1 |
| Izod impact strength, parallel |
 |
ISO 180/2A |
≥5,0 mm |
55 |
KJ/m2 |
* 1 |
| Shearing strength, parallel |
 |
IEC 60893-2 |
≥5,0 mm |
55 |
MPa |
* 1 |
| Tensile strength |
|
ISO 527 |
≥1,6 mm |
320 |
MPa |
* 1 |
|
| Electrical properties |
|
Testmethod |
Thickness |
Value |
Unit |
|
| Electric strength in oil at 90°C |
 |
IEC 243-1 |
3,0 mm |
20 |
kV/mm |
* 2 |
| Electric strength in oil at 90°C |
 |
IEC 243-1 |
≥3,0 mm |
60 |
kV/25mm |
* 2 |
| Permittivity 50 Hz |
|
IEC 250 |
≤3,0 mm |
4,0 |
|
* 3 |
| Permittivity 1 MHz |
|
IEC 250 |
≤3,0 mm |
- |
|
- |
| Dissipation factor 50 Hz |
|
IEC 250 |
≤3,0 mm |
0,01 |
|
* 3 |
| Dissipation factor 1 MHz |
|
IEC 250 |
≤3,0 mm |
- |
|
- |
| Insulation resistance after immersion in water |
|
IEC 167 |
All |
500.000 |
MΩ |
* 4 |
| Comparative tracking index |
|
IEC 112 |
≥3,0 mm |
250 |
CTI |
* 1 |
|
| Physical and thermal properties |
|
|
Testmethod |
Thickness |
Value |
Unit |
|
| Thermal endurance index 20.000 h |
|
IEC 216 |
≥3,0 mm |
200 |
T.I. |
- |
| Flammability |
|
IEC 707 |
≥ 4,0 mm |
F V0 |
|
* 1 |
| Density |
|
IEC 1183-A |
All |
1,95 |
g/cm3 |
* 1 |
| Water absorption |
|
IEC 62-1 |
50x50x3 mm |
25 |
mg |
* 4 |
|
| Characteristics and applications |
|
| The most temperature-resistant material of all types. Retains its outstanding mechanical properties even at very high application temperatures. Used as thermal insulation plates in moulds, dies, casting tools, presses and similar where the requirements for compression strength and temperature resistance are rigorous. See the graph. |
|
|
|
Notes:
A) Thickness > 8mm.
B) Thickness ≥ 4,0mm
C) 1 h/130°C / measured at 130°C
D) 1 h/150°C / measured at 150°C
E) 1 h/180°C / measured at 180°C
F) 1 h/200°C / measured at 200°C
|
* Conditioning:
1: 24h/23°C/50%RH
2: 24h/23°C/50%RH + 1h/Oil 90°C
3: 96h/105°C + 1h/23°C/20%RH
4: 24h/50°C + 24h/water 23°C
5: 96h/105°C + 1h/Oil 90° |
|
|
|
| The above values are average values based on the results of extensive testing in our laboratories. ELEKTRO-ISOLA A/S cannot accept responsibility for the performance of our products in applications over which we have no control. |
|
|